| Stress corrosion crack initiation of alloy 600 in PWR primary water Z Zhai, MB Toloczko, MJ Olszta, SM Bruemmer Corrosion Science 123, 76-87, 2017 | 46 | 2017 |
| Precursor evolution and stress corrosion cracking initiation of cold-worked alloy 690 in simulated pressurized water reactor primary water Z Zhai, M Toloczko, K Kruska, S Bruemmer Corrosion 73 (10), 1224-1236, 2017 | 45 | 2017 |
| Effects of phosphorus segregation on stress corrosion cracking in the heat-affected zone of a dissimilar weld joint between a Ni-base alloy and a low alloy steel Z Zhai, H Abe, Y Miyahara, Y Watanabe Corrosion Science 92, 32-42, 2015 | 23 | 2015 |
| Stress corrosion crack initiation measurements of alloy 600 in PWR primary water MB Toloczko, MJ Olszta, Z Zhai, SM Bruemmer 17th International Conference on Environmental Degradation of Materials in …, 2015 | 21 | 2015 |
| Failure probabilistic analysis of steam generator heat-transfer tubing with pitting corrosion BH Zhou, ZQ Zhai Engineering Failure Analysis 18 (5), 1333-1340, 2011 | 21 | 2011 |
| Achieving ASIL D for microcontroller in safety-critical drive-by-wire system Z Zhai, T Corbiere SAE Technical Paper, 2009 | 16 | 2009 |
| Segregation behavior of phosphorus in the heat-affected zone of an A533B/A182 dissimilar weld joint before and after simulated thermal aging Z Zhai, Y Miyahara, H Abe, Y Watanabe Journal of Nuclear Materials 452 (1-3), 133-140, 2014 | 15 | 2014 |
| Precursor corrosion damage and stress corrosion crack initiation in alloy 600 during exposure to PWR primary water Z Zhai, MJ Olszta, MB Toloczko, SM Bruemmer 17th International Conference on Environmental Degradation of Materials in …, 2015 | 11 | 2015 |
| Characterization of stress corrosion cracking initiation precursors in cold-worked alloy 690 using advanced high-resolution microscopy K Kruska, Z Zhai, DK Schreiber, SM Bruemmer Corrosion 75 (7), 727-736, 2019 | 10 | 2019 |
| Crack Initiation Behavior of Cold-Worked Alloy 690 in Simulated PWR Primary Water-Role of Starting Microstructure, Applied Stress and Cold Work on Precursor Damage Evolution Z Zhai, MJ Olszta, MB Toloczko, SM Bruemmer Pacific Northwest National Lab.(PNNL), Richland, WA (United States), 2019 | 5 | 2019 |
| Material Condition Effects on Stress Corrosion Crack Initiation of Cold-Worked Alloy 600 in PWR Primary Water Environments Z Zhai, MB Toloczko, SM Bruemmer M3LW-19OR0402037, Pacific Northwest National Laboratory, 2019 | 5 | 2019 |
| Characterization of SCC initiation precursors in cold-worked alloy 690 K Kruska, Z Zhai, SM Bruemmer NACE CORROSION, NACE-2017-9717, 2017 | 5 | 2017 |
| Effects of thermal history and microstructure on segregation of phosphorus and alloying elements in the heat-affected zone of a low alloy steel Z Zhai, Y Miyahara, H Abe, Y Watanabe Metallurgical and Materials Transactions A 45, 6163-6172, 2014 | 5 | 2014 |
| Microstructural Effects on SCC Initiation in PWR Primary Water for Cold-Worked Alloy 600 Z Zhai, M Toloczko, S Bruemmer Proceedings of the 18th International Conference on Environmental …, 2019 | 4 | 2019 |
| Lifetime distribution model of port facilities with pitting corrosion of stochastic processes BH Zhou, ZQ Zhai Applied Mechanics and Materials 44, 46-50, 2011 | 4 | 2011 |
| Grain Boundary Damage Evolution and SCC Initiation of Cold-Worked Alloy 690 in Simulated PWR Primary Water Z Zhai, M Toloczko, K Kruska, D Schreiber, S Bruemmer Proceedings of the 18th International Conference on Environmental …, 2019 | 3 | 2019 |
| Stochastic process-based modeling method for pitting corrsion of Ni-based alloy 690 ZBZ Ziqing Acta Metall Sin 47 (9), 1159-1166, 2011 | 3 | 2011 |
| Examination of Cavity Formation in Cold-Worked Alloy 690 MJ Olszta, Z Zhai, MB Toloczko, SM Bruemmer Pacific Northwest National Lab.(PNNL), Richland, WA (United States), 2019 | 2 | 2019 |
| Stochastic-process-based modeling method of pitting corrosion for port machinery ZQ Zhai, B ZHOU Computer Integrated Manufacturing System 16 (10), 0, 2010 | 2 | 2010 |
| Long-Term Crack Initiation Behavior of Cold-Worked Alloy 690 in PWR Primary Water Z Zhai, M Toloczko, S Bruemmer NACE CORROSION, D041S018R008, 2021 | 1 | 2021 |